S355J2H Pipe
S355J2H Pipe
The letter H is a designation intended for hollow sectioned products like the
S355J2H Pipe. The other designation that touches the base with regards to its
application is the letter S, which is a typical feature of structural steels.
There are several reasons as to why the EN 10210 S355J2H Seamless Pipe exhibits
good impact strength. Firstly, the chemistry of the carbon steel group contains
manganese, which not only improves its strength but also improves the hardness
properties of the S355J2H EN 10210 Pipes. Secondly, in comparison to regular
pipes, hollow sections have thicker walls. A thicker cross-section also makes EN
10210 Grade S355J2H Hot Finished CHS sturdy and very durable.
.
Specification
| Property | Value |
|---|---|
| Grade | S355J2H |
| Material Type | Seamless Steel Pipe |
| Material Standard | EN 10210-1, EN 10210-2 |
| Material Composition | Carbon, Silicon, Manganese, Phosphorus, Sulfur |
| Yield Strength | ≥ 355 MPa |
| Tensile Strength | 510 - 680 MPa |
| Elongation | ≥ 22% (in 200 mm) |
| Impact Strength | ≥ 27 Joules at -20°C |
| Charpy V-notch Impact Test | Longitudinal test specimen, 27 Joules minimum at -20°C |
| Applications | Structural applications in construction, machinery, and engineering |
| Manufacturing | Hot finished seamless pipes |
| Sizes | Various sizes and thicknesses as per EN 10210 standards |
 |
 |
 |
 |